ИСТИНА

Porous ceramics (ZrO2, alumina etc.) are widely used as catalysts support. Synthesis of oxides with hierarchical porous structure is of great importance in order to provide the accessibility of active sites to reagents. To create mesoporous structure organic templates are widely used. Prepared oxide materials are then impregnated by active metal precursor followed by metal reduction. In this work one-pot synthesis of Ni-ZrO2 composites with wood templates are studied. Study of textural properties of prepared samples revealed mesoporous structure of biomorphous samples. Segregation of Ni particles is observed by TPR during Red-Ox treatment. Prepared Ni_ZrO2 composites shows high catalytic activity in reductive transformations of chlorobenzenes. Утилизация хлорорганических загрязнителей в биосфере является актуальной задачей. Одним из перспективных способов их переработки в полезные вещества является каталитическое гидродехлорирование (ГДХ). Известно, что нанесенные на ZrO2 никелевые катализаторы проявляют высокую активность и стабильность в ГДХ. В литературе существует информация, что восстановление бинарных оксидов NiO-ZrO2 приводит к получению высокодисперсного никеля на поверхности носителя, обеспечивая высокую активность катализатора. Отмечается, что высокая гомогенность в многокомпонентных системах может быть достигнута при синтезе образцов с использованием структурных темплатов [1]. В работе приготовлен бинарный оксид NiO-ZrO2, содержащий 11,81 мольн.% NiO и чистый оксид циркония. Синтез образцов осуществлялся с применением в качестве темплата природного объекта–древесины [2]. Системы, полученные таким способом, в измененном масштабе копируют морфологию и текстуру биотемплата и получили в литературе название биоморфных. На рис.1 представлены электронные микрофотографии биоморфных оксидов. Из