Synthesis and properties of zirconium-doped RbTiOPO4 single crystalsстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Single crystals of the solid solutions RbTi1-xZrxOPO4 (0.015 < x < 0.034) were grown and their physical properties were studied. In the presence of zirconium in the crystals with the maximum content x = 0.034, the ferroelectric phase transition and the high-temperature transition from the orthorhombic to the cubic phase are shifted to lower temperatures by 100 and 50 degrees C, respectively. In the temperature range from 700 degrees C to room temperature, the conductivity of doped crystals decreases compared to that of the undoped crystals. It is of particular interest that the intensity of the second-harmonic generation of the doped crystals is substantially higher than that of RbTiOPO4.