Magnetic ordering and coercivity of {Y, Tb}Ni4Si, NdNi3TSi (T = Mn - Cu) and Sm1-xTbxNi3FeSi solid solutionsстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 4 сентября 2018 г.
- Авторы: Morozkin A.V., Garshev A.V., Yapaskurt V.O., Jinlei Yao, Nirmala R., Quezado S., Malik S.K.
- Журнал: Journal of Solid State Chemistry
- Том: 265
- Год издания: 2018
- Издательство: Elsevier B.V.
- Местоположение издательства: Netherlands
- Первая страница: 18
- Последняя страница: 28
- DOI: 10.1016/j.jssc.2018.05.019
- Аннотация: Magnetic ordering of the polycrystalline YNi4Si-type YNi4Si, disordered YNi4Si-type TbNi4Si and NdNi3CoSi (space group Cmmm, N 65, oC12), and CaCu5-type NdNi3TSi (T = Mn, Fe, Cu) and Sm1-xTbxNi3FeSi (x = 0.25 and 0.5) solid solutions (space group P6/mmm, N 191, hP6) have been studied by magnetization measurements. Down to 2 K, YNi4Si is paramagnetic, whereas TbNi4Si, NdNi3MnSi, NdNi3FeSi, NdNi3CoSi and NdNi3CuSi show ferromagnetic ordering (TC) at 30 K, 71 K, 120 K, 20 K and 5.6 K and field sensitive transitions (Tm) at 10 K, 43 K, 63 K, 16 K and 3.8 K, respectively. Sm0.75Tb0.25Ni3FeSi and Sm0.5Tb0.5Ni3FeSi show ferromagnetic-antiferromagnetic transformations below ferromagnetic ordering at 166 K and 120 K, respectively. Magnetocaloric effect (MCE) of TbNi4Si, NdNi3{Mn, Co, Cu}Si, Sm0.75Tb0.25Ni3FeSi and Sm0.5Tb0.5Ni3FeSi compounds were estimated in terms of isothermal magnetic entropy change (deltaSm). Among these compounds, TbNi4Si and NdNi3CuSi show maximal MCE with deltaSm of -9.95 J/kg·K (RCP50kOe ~ 180 J/kg) at 26 - 30 K and -6.29 J/kg·K (RCP50kOe ~ 31 J/K) at 6 K in a field change of 50 kOe, respectively. Below Tm, TbNi4Si, NdNi3MnSi, NdNi3FeSi, NdNi3CoSi, NdNi3CuSi and Sm0.5Tb0.5Ni3FeSi show hard magnetic properties with coercivity of 2.2 kOe, 4.8 kOe, 4.8 kOe, 9.5 kOe, 1 kOe and 15 kOe at 2 K, respectively. Sm0.75Tb0.25Ni3FeSi shows a coercivity of 39 kOe at 40 K.