Soft magnetism in nitrided Fe93Ni4Cr3 and Fe94Ni4T2 cold-rolled alloysстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:The magnetic properties in relation with the structure of nitrided cold-rolled Fe93Ni4Cr3 and Fe94Ni4Ti2 were studied. Various low-temperature nitriding treatments were applied in order to obtain soft magnetic materials. We show that the magnetic anisotropy depends sensitively on the nitrogen content. The lowest value of the coercive force, H-C = 40 A/m was obtained for samples containing TiN precipitates. For the Cr contained samples, a concentration of 14% (FeNi)(4)N (gamma’)-phase decreases H-C below values corresponding to the samples containing only CrN precipitates. We discuss the influence of the texture on the magnetic properties of samples containing only BCC alpha’-phase, a mixture of alpha’ + gamma’-phase, or samples which have been cycled through the epsilon-phase. Although grain refinement is observed after cycling and an almost random orientation of the grains is obtained, the magnetic properties do not improve. This is due to the fact the grain size is still too large to lead to averaging out of the magnetic anisotropy. Moreover, the stress/strain distribution developed during the treatments hampers domain wall motion and leads to an increased coercivity. (C) 2002 Elsevier Science B.V. All rights reserved.