3 PHASES IN THE SYSTEM HG1-XCXBA2CUOY (0.00-LESS-THAN-OR-EQUAL-TO-X-LESS-THAN-OR-EQUAL-TO-1.00)статья
Информация о цитировании статьи получена из
Scopus,
Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Samples of the [Hg1-xCx]-Ba(2)CuOy system [(Hg,C)-1201] with stoichiometries within the range 0.00 less than or equal to x less than or equal to 1.00 were synthesized by a high-pressure, high-temperature technique. The sample with x = 0.00 [HgBa2CuO4+delta] was non-superconducting with lattice parameters a = 3.8676(2) Angstrom, c = 9.470(1) Angstrom. At low ranges of substitution (0.10 less than or equal to x less than or equal to 0.30), the predominant phase was found to be Hg-1201 with identical lattice parameters to those found for x = 0.00. At x = 0.40 the Hg-1201 phase coexists in similar proportions with the phase of mixed [Hg-1-x,C-x]-1201 stoichiometry. At x = 0.50, this second phase with lattice parameters a = 3.9271(3) Angstrom, c = 8.676(2) Angstrom is predominant and only traces of the Hg-1201 phase were found. At x = 0.75 the [Hg-1-x,C-x]-1201 phase found for x = 0.50 coexists with the CO3Ba2CuOy phase, which is the extreme of the substitution range. This latter was predominant at x = 1.00 with lattice parameters a = 4.0044(3) Angstrom, c = 7.909(1) Angstrom, but at higher pressure than the previous substitutions. This system is constituted of three main phases, HgBa2CuO4+delta, Hg1-xCxBa2CuOy (x = 0.50) and CO3Ba2CuOy, which appear in different proportions according to the percentage of substitution and the applied synthesis pressure.