Electrochemical intercalation in the graphite-H2SO4-R (R=CH3COOH, H3PO4) systemстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:The anodic oxidation of highly oriented pyrolitic graphite (HOPG) in the mixture H2SO4-R (R=CH3COOH, H3PO4) with concentration of H2SO4 in the range 0-100 wt% was investigated in this research work. Galvanostatic oxidation of graphite in H2SO4-R solution allows one to obtain stages 1-5 graphite intercalation compounds (GICs). The presence of R in the electrolyte solutions significantly expands the concentration limit for intercalation down to 1 wt% of H2SO4. The co-intercalated stages 1 and 2 H2SO4-CH3COOH-GICs with d(i) = 7.94 Angstrom were obtained in 60-80 wt% of H2SO4 Solution. The stages 1-3 co-intercalated H2SO4-H3PO4-GICs with d(i) = 8.08-8.20Angstrom were synthesized for the first time. It was shown that the form of galvanostatic curve E(Q) is determinated by the content of strong intercalate H2SO4. It was established that the potential of intercalation E-int of the stages 1-3 co-intercalated GICs and the quantity of electricity (Q) are higher than E-int and Q for the formation of binary GICs (graphite hydrogen sulfate). The enhancement of the potential barrier for intercalation gives the evidence of the co-intercalation of H2SO4 with CH3COOH or H3PO4 in graphite matrix. The mechanism of co-intercalation of graphite was proposed.