Hall effect and magnetoresistance in rapidly quenched Fe-B ribbonsстатья
Информация о цитировании статьи получена из
Scopus,
Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:The Hall effect and transverse magnetoresistance (MR) in amorphous ferromagnetic alloys Fe100-xBx with x=12.2-18.1 at% have been studied at 77-300 K. It was found that the ordinary and extraordinary Hall coefficients, R(o) and R(s), are equal to R(o)=(20-70)x10(-12) Wcm G(-1) and R(s)=(6-9)x10(-10) Wcm G(-1), depend on temperature (dR(o)/dT <0, dR(s)/dT <0) and display a non-monotonic dependence on composition, with extrema at x=14.4 at%. It was established that for amorphous and crystalline alloys the typical relation between R(s) and the resistivity is not fulfilled in amorphous alloys Fe-B. In the case of a magnetic field perpendicular to the ribbon plane, the transverse MR is positive up to 8-10 kOe. The most pronounced positive effect exists in alloys with 13.1 at% at similar to 180 K. Possible reasons for the unusual behaviour of R(s) and the MR are discussed.