Thermoelectric properties of low-cost transparent single wall carbon nanotube thin films obtained by vacuum filtration

Tambasov, I.A.; Voronin, A.S.; Evsevskaya, N.P.; Volochaev, M.N.; Fadeev, Y.V.; Simunin, M.M.; Aleksandrovsky, A.S.; Smolyarova, T.Е.; Abelian, S.R.; Tambasova, E.V.; Gornakov, M.O.; Eremina, V.A.; Kuznetsov, Y.M.; Dorokhin, M.V.; Obraztsova, E.D.

Авторы: Tambasov I.A., Voronin A.S., Evsevskaya N.P., Volochaev M.N., Fadeev Y.V., Simunin M.M., Aleksandrovsky A.S., Smolyarova T.Е., Abelian S.R., Tambasova E.V., Gornakov M.O., Eremina V.A., Kuznetsov Y.M., Dorokhin M.V., Obraztsova E.D.
Журнал: Physica E: Low-Dimensional Systems and Nanostructures
Том: 114
Год издания: 2019
Издательство: Elsevier BV
Местоположение издательства: Netherlands
Первая страница: 113619 -1
Последняя страница: 113619 -10
DOI: 10.1016/j.physe.2019.113619
Аннотация: The dispersions of semiconducting (sc-) and metallic (m-) SWCNTs with purity more than 98 and 86 %, correspondingly, were obtained by using the aqueous two-phase extraction method.The unseparated (un-) SWCNTs contained ~ 3/4 of semiconducting and ~ 1/4 of metallic nanotubes. Thin films based on unseparated, semiconducting and metallic SWCNTs were prepared by vacuum filtration method. An Atomic Force Microscopy (AFM) and a Transmission Electronic Microscopy (TEM) were used to investigate the thin film microstructure. The thin SWCNT film transmittance was measured in the wavelength range of 300 -1500 nm.Thermoelectric properties were carried out in the temperature range up to 200 0C. The largest Seebeck coefficient was observed for thin films based on semiconducting SWCNTs. The maximum value was 98 μV/K under the temperature of 170 0C. The lowest resistivity was 7.5·10-4·Ohm·cm at room emperatureA fCoCr tEhPinT EunD-S MWACNNUTS fCilmRIsP. TThe power factor for m-SWCNT and un-SWCNT films was 47 and 213 μW·m-1·K-2, correspondingly, at room temperature and 74 and 54 μW·m-1·K-2 at 200 0C, respectively. For a thin sc-SWCNT film the maximum power factor was 2.8 μW·m-1·K-2 at 160 0C. The un-SWCNT film thermal conductivity coefficient was 5.63 and 3.64 W·m-1·K-1 and a thermoelectric figure of merit was 0.011 and 0.016 at temperatures of 23 and 50 0C, respectively.
Добавил в систему: Образцова Елена Дмитриевна

	ИСТИНА	Войти в систему Регистрация
	ИСТИНА ИНХС РАН
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

ИСТИНА ИНХС РАН

Thermoelectric properties of low-cost transparent single wall carbon nanotube thin films obtained by vacuum filtrationстатья

Прикрепленные файлы