Towards a new group of olivine-type afterglow phosphors: the case of Ca2GeO4:Dy3+статья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 1 августа 2019 г.
Аннотация:Powder XRD confirms that Ca2−3xDy2xGeO4 (x = 0.00, 0.01, 0.025, 0.04) synthesized by ceramic route crystallize with the olivine-type unit cell (space group Pnma, Z = 4). The trivalent dysprosium ions occupy two crystallographically nonequivalent sites (4a) and (4c) with the Ci and Cs symmetry, respectively. Raman spectroscopy corroborates the crystal structure features of orthorhombic Dy3+-doped Ca2GeO4 with the maximum phonon energy of 760 cm−1. The phosphors with optimal dopant concentration of 1 at% exhibit yellow emission under 349 nm excitation and white afterglow for more than 1 h after 240 nm excitation for 5 min.