Stabilization of gas transport properties of PTMSP with porous aromatic framework: effect of annealingстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 15 декабря 2016 г.
Аннотация:This work was focused on the study of physical aging of PTSMP and preventing this effect via incorporation of porous aromatic frameworks (PAF-11). The dense PTMSP membranes with PAF-11 content of 0, 1, 5 and 10 wt % were stepwise annealed in air at 100 °C for up to 510 hours with constant monitoring of O2, N2 and CO2 permeability (measured at 30 °C). As-cast and aged PTMSP samples were characterized by means of helium pycnometry, dynamic mechanical analysis and IR spectroscopy. Gas transport characteristics of the PTMSP sample containing 10 wt % of PAF-11 became stable upon annealing at 100 °С within the short time interval (100-200 hours). However, for all other samples containing 5 wt % of PAF-11 or less, gas permeability gradually decreased with time. According to the IR analysis, upon high-temperature treatment, PAF-11 nanoparticles tended to migrate from the sub-layer region into the membrane matrix bulk. According to the helium picnometry, the introduction of PAF-11 to the PTMSP matrix provided a loosened packaging of polymer chains, and the structure became more stabilized since the porous filler served as a “physical” cross-linker.