Phase Transformations Occurring during Preparation of Ordered Ternary Fe-Al-M Alloys (with M = Ga, B, V, and Mn) by Mechanical Alloying Автор:: G.; с соавторамистатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 20 января 2021 г.
Аннотация:The possibility of synthesis of the ordered ternary Fe65Al35 - (x)\M-x and Fe-65 - yAl35My alloys with x, y = 0, 3, 5, 10 at % and M = B, Ga, V, Mn is studied and conditions of the synthesis are reported. Nanocrystalline metastable disordered ternary alloys are used as the precursor materials for the ordered alloys, which are prepared by mechanical alloying from elemental components. The heat treatment of mechanically alloyed compositions allowed us to reach the single-phase state with the B2 superstructure for the compositions with Ga and V; the single-phase state with the D0(3) superstructure was reached for the compositions with B and Mn.