Glass-ceramic synthesis of Cr-substituted strontium hexaferrite nanoparticles with enhanced coercivityстатьяИсследовательская статья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 4 июня 2021 г.
Аннотация:Magnetically hard ferrites attract considerable interest due to their ability to maintain a high coercivity of nanosized particles and therefore show promising applications as nanomagnets ranging from magnetic recording to biomedicine. Herein, we report an approach to prepare nonsintered single-domain nanoparticles of chromium-substituted hexaferrite via crystallization of glass in the system SrO–Fe2O3–Cr2O3–B2O3. We have observed a formation of plate-like hexaferrite nanoparticles with diameters changing from 20 to 190 nm depending on the annealing temperature. We demonstrated that chromium substitution led to a significant improvement of the coercivity, which varied from 334 to 732 kA m−1 for the smallest and the largest particles, respectively. The results provide a new strategy for producing high-coercivity ferrite nanomagnets.