Аннотация:The production of a precursor of magnesium aluminate spinel (AMS) by thermic synthesis to obtain a material with high-performance properties is reviewed in the work. The temperature synthesis of AMS is determined, the introduction of the additive is described in the range of concentrations of 3, 5, and 7 mol.%. The current processes during the firing of products have been investigated with a view to the further selection of the firing mode of the ceramic samples, which can be obtained.