Preparation and properties of fine BaCeO3 powders for low-temperature sinteringстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Detailed characterization of BaCeO3 powders prepared through different chemical homogenization processes demonstrates that pyrolysis of coprecipitated oxalates ensures the smallest crystallite size and the highest rate of phase formation among the processes examined. Increasing the heating rate during the thermal decomposition of oxalates reduces the average crystallite size and the strength ofagwregates in the powder. Sintering of the resultant barium cerate powders at 1000 degrees C in the presence of, cupric oxide enables the preparation of ceramics with a density above 90% of theoretical density. The low-temperature liquid-phase sinterability of BaCeO3 powders depends crucially on the presence of residual impurity phases, which notably reduce the shrinkage rate.