Preparation of magnetic glass-ceramics through glass crystallization in the Na2O-SrO-Fe2O3-B2O3 systemстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Glasses with the nominal compositions SrFe12O19 + nNa(2)Sr(2)B(4)O(9) (n = 4, 6, 8, 10) and SrFe12O19 + 6Na(2)Sr(3)B(4)O(10) were prepared via rapid quenching of oxide melts and were then heat-treated between 500 and 800 degrees C in order to produce glass-ceramics containing fine SrFe12O19 particles. The materials were characterized by x-ray diffraction, differential thermal analysis, electron microscopy, and magnetic measurements. The crystallization behavior of the glasses was investigated. The coercivity of the glass-ceramics was shown to increase with heat-treatment temperature, up to 486 kA/m. By dissolving the nonmagnetic matrix of the glass-ceramics with the nominal compositions SrFe12O19 + 6Na(2)Sr(3)B(4)O(10) and SrFe12O19 + 4Na(2)Sr(2)B(4)O(9), submicron-sized strontium hexaferrite particles were obtained.