Аннотация:The electrical conductivity of azolectine bilayer lipid membranes is observed to increase 10–40-fold with respect to its background value of 67 ± 13 pS/mm2 upon the addition of cubic CoFe2O4 nanoparticles with the main diagonal of 14 nm (MNP-14) and 27 nm (MNP-27). As the concentration of MNP-14 in the membrane solution increases from 50 to 450 µg/mL, the increase in the membrane conductivity with respect to its background value is nonlinear and can be approximated by the exponential dependence with exponent 2.75. Discrete current pulses are observed in the constant voltage mode for the MNP-14 concentration higher than 250 µg/mL and for all MNP-27 concentrations starting from 50 µg/mL, which points to the appearance of conducting lipid pores.