Аннотация:А new kind of modified thermoset resins were synthesized by phase-transfer Williamson reaction from novolac resin and mixtures of allyl- and propargyl chlorides. The compositions of the resins were defined by 1H NMR spectroscopy and the dependence of the cured materials properties on the composition was established. Increase of a propargyl content resulted in char yield raise and the maximum value had been found for propargylated resin—58%. DSC (differential scanning calorimetry)-analysis of the resins has demonstrated that exothermic enthalpy of the curing process could be adjusted by varying the content of propargyl and allyl groups in the resin