Ferromagnetism of Mn-implanted silicon: Magnetization and magnetooptic Faraday effectстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Manganese-implanted silicon plates of both n and p types have been obtained by implanting 195-keV manganese ions with doses from 1 x 10(15) to 2 x 10(16) cm(-2). According to magnetic measurements by a vibrating sample magnetometer and a SQUID magnetometer, all of the samples exhibit a ferromagnetic ordering at room temperature. The magnetooptic Faraday effect is manifested in the spectral region 1-6 mu m in the temperature interval 80-305 K. The characteristic features of the field and temperature dependences of magnetization and the spectrum of the Faraday effect indicate a percolation type of magnetic ordering at low temperatures and a crucial role of the exchange between delocalized p-type carriers and Mn ions at temperatures above 100 K.