A novel process for textured thick film YBa2Cu3Oy coated conductors based on a constitutional gradients principleстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:A new method for the processing of textured YBa2CuOy (Y123) thick film stripes on metallic tapes is discussed. The process involves the texturing of Y123 grains by a localized directional solidification method by creating constitutional gradients along the width of the precursor Y2BaCuO5 (Y211) stripe during an infiltration and growth process. The differences in the solidification temperatures of different rare earth 123 compounds were utilized to generate the constitutional gradients. The sample configuration involves printed lines of light (Nd) and heavy (Yb) rare earth compounds on either side of an airbrushed Y211 stripe underneath a liquid phase (barium cuprates) layer. The higher peritectic temperature (T-p) Nd regions serve as nucleating sites for Y123 grains nucleated in the adjacent Y211 stripes and the constitutional gradients produced due to the diffusion of respective rare earth ions between the Nd and Yb regions, typically of 200 K cm(-1) in the region, induce a driving force for the directional growth of the nucleated grains. The solidification is analogous to that in a typical Bridgman furnace in applied high temperature gradients. The process, being independent of growth rate parameter and texture of the underlying substrate, is suitable for the fabrication of long length thick film conductors by a wind and react process in simple box type furnaces.