Аннотация:Electrochemical behaviour of 4.8 ± 0.2 nm graphene films on nickel and copper foams was investigated by cyclic voltammetry (CV). The graphene films were prepared by chemical vapor deposition and characterized by electron energy loss spectroscopy, elastic peak electron spectroscopy, scanning electron microscopy and X-ray photoelectron spectroscopy. The CV of the [Ru(NH3)6]+2/+3 redox reaction was performed using these substrates. The obtained results demonstrated a high continuity of the deposited graphene film and independence of the electron transfer rate on them from the metal substrate used. The rate of outer-sphere electron transfer on the graphene surface appeared to be substantially less than that on the polished glassy carbon. Partial splitting of graphene layers due to wedged action of 2D adsorption layers, formed by camphor solution, led to the increase in double-layer capacitance.