Polymer electrolyte based on Nafion plasticized with carbonates and their ternary mixtures for sodium-ion batteries

Kayumov, R.R.; Radaeva, A.P.; Nechaev, G.V.; Lochina, A.A.; Lapshin, A.N.; Bakirov, A.V.; Glukhov, A.A.; Shmygleva, L.V.

Авторы: Kayumov Ruslan R., Radaeva Alena P., Nechaev Grigory V., Lochina Anna A., Lapshin Alexander N., Bakirov Artem V., Glukhov Alexander A., Shmygleva Lyubov V.
Журнал: Solid State Ionics
Том: 399
Год издания: 2023
Издательство: Elsevier BV
Местоположение издательства: Netherlands
Первая страница: 116294
Последняя страница: 116304
DOI: 10.1016/j.ssi.2023.116294
Аннотация: The physicochemical properties and ionic conductivity of Nafion polymer membrane in sodium form plasticized with such organic solvents as ethylene carbonate (EC), propylene carbonate (PC), dimethyl carbonate (DMC) and their ternary mixtures were studied. According to the results of gravimetry, simultaneous thermal analysis, IR spectroscopy, small-angle X-ray scattering, voltammetry, and impedance spectroscopy, it was shown that the optimal plasticizer for Na-Nafion membrane among the studied systems is a ternary mixture with the composition EC/PC/DMC = 0.45/0.45/0.1. The polymer electrolyte based on Na-Nafion, plasticized with this ternary mixture, despite the lower electrochemical stability compared to the membrane swollen with EC, has the highest swelling degree of 31% and the ionic conductivity of 0.08 mS cm−1 at 20 °C, which is maintained even at −60 °C (6 × 10−8 S cm−1). The obtained values are comparable with the conductivity of the lithium form of Nafion. The possibility of using a membrane based on the sodium form of Nafion as an electrolyte in sodium and sodium-ion batteries was shown.
Добавил в систему: Шмыглева Любовь Вячеславовна

	ИСТИНА	Войти в систему Регистрация
	ИСТИНА ИНХС РАН
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

ИСТИНА ИНХС РАН

Polymer electrolyte based on Nafion plasticized with carbonates and their ternary mixtures for sodium-ion batteriesстатья

Прикрепленные файлы