Structure–Phase Transitions in the Friction Contact Zone of High-Nitrogen Chromium–Manganese Austenitic SteelстатьяИсследовательская статья
Информация о цитировании статьи получена из
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 15 февраля 2024 г.
Аннотация:Abstract: The influence of contact stresses on the phase and concentration composition of thin surface layers and wear products in the tribological contact zone of high-nitrogen FeMn22Cr18N0.83 steel was studied using Mössbauer spectroscopy, X-ray structural analysis, and electron microscopy. It was shown that contact compressive stresses developing under the conditions of dry sliding friction in the surface layers (20–25 microns) resulted in the strain-induced dissolution of cellular precipitation products (nitrides Cr2N) and increased the average content of nitrogen in austenite. Antiferromagnetic ordering in austenite caused by the precipitation of secondary nitrides with low chromium and nitrogen content was observed in tiny external layers (~0.1 microns) of the friction surface and products of steel adhesive wear. The effect of tension stresses in the friction contact zone on the formation of strain-induced martensite and nitrides with 00-Fe16N2 structures was established in the wear products.