Microwave Properties of FeCo–SiO2 Systems Obtained by High-Energy Millingстатья
Информация о цитировании статьи получена из
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 23 ноября 2017 г.
Аннотация:Structural and phase composition and magnetostatic and microwave properties of Fe70Co30–SiO2
systems obtained by high-energy milling in acetone for different times (from 6 to 48 h) are studied. It is found that, after the longest milling time, the obtained particles have sizes from 0.5 to 5 μm, are covered with a thin layer of SiO2, and contain 10 wt % iron carbides. Milling-induced change in the phase composition of the particles influences their specific magnetization of saturation and coercive force, but has a small effect on the microwave
permittivity of composite materials containing these particles in the frequency range of 0.1–6 GHz. As the milling time grows, the imaginary part of the microwave permeability decreases at frequencies below 1 GHz.