Аннотация:Single-crystals of Co8.4Al9.4W1.9Ta alloy with macrosegregation of Al and W were directionallysolidified with a flat front. Mini-specimens of different composition were cut at differentheights of the single-crystals and tested for compression and oxidation at 900°C. It was found that Wincreases yield strength while Al retards oxidation.