On the possibility of reducing oxidation temperature of low-carbon steel in nitrate solutionsстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 8 декабря 2017 г.
Аннотация:The effect of different additions on the protective properties of a magnetite coating prepared by the oxidation of low-carbon steel in nitrate solution at 70-98A degrees C is studied using physical, electrochemical, and corrosion methods. The introduction of the developed addition URMP-5 to ammonium nitrate solution is shown to yield coatings with good protective properties, not only at 98A degrees C, but also at 70A degrees C. The further treatment of oxidized steel product with passivating compositions creates new fields for their using, even in the presence of direct atmospheric precipitations.