Acid–Base Properties of Macroporous Weak Base Anionite Based on Aminated Acrylonitrile/Divinylbenzene Copolymer

Meichik, N.R.; Veretennikovaa, G.V.; Nikolaeva, Y.I.; Svetneva, O.B.; Stepanov, S.I.

Авторы: Meichik N.R., Veretennikovaa G.V., Nikolaeva Yu I., Svetneva O.B., Stepanov S.I.
Журнал: Polymer Science, Series B
Том: 59
Номер: 6
Год издания: 2017
Издательство: Pleiades Publishing, Ltd
Местоположение издательства: Road Town, United Kingdom
Первая страница: 737
Последняя страница: 740
Оригинальные версии: Кислотно-основные свойства макропористого низкоосновного анионита на основе аминированного сополимера акрилонитрила с дивинилбензолом , КИСЛОТНО-ОСНОВНЫЕ СВОЙСТВА МАКРОПОРИСТОГО НИЗКООСНОВНОГО АНИОНИТА НА ОСНОВЕ АМИНИРОВАННОГО СОПОЛИМЕРА АКРИЛОНИТРИЛА С ДИВИНИЛБЕНЗОЛОМ , КИСЛОТНО-ОСНОВНЫЕ СВОЙСТВА МАКРОПОРИСТОГО НИЗКООСНОВНОГО АНИОНИТА НА ОСНОВЕ АМИНИРОВАННОГО СОПОЛИМЕРА АКРИЛОНИТРИЛА С ДИВИНИЛБЕНЗОЛОМ
DOI: 10.1134/S1560090417060033
Аннотация: Potentiometric titration of weak base anionite (the degree of crosslinking was 12–16%) was performed within the pH range of 2–12 and NaCl concentration range of 0.1–1.0 mol/L. The maximum ionexchange ability against HCl does not depend on the solution ionic strength and is 6.50 ± 0.12 mmol/g of dry solid matter. It was shown that the process of acid–base equilibrium can be adequately described by the Gregor equation within the studied stock electrolyte concentration and pH ranges. Two type of groups were discovered in anionite. The ionization constants of these groups differ by three orders of magnitude. The existence of amino groups of different nature was proved by the data obtained by functional analysis; it was estimated that the acidity of these groups decreases as NaCl concentration increases.
Добавил в систему: Мейчик Наталия Робертовна

	ИСТИНА	Войти в систему Регистрация
	ИСТИНА ИНХС РАН
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

ИСТИНА ИНХС РАН

Acid–Base Properties of Macroporous Weak Base Anionite Based on Aminated Acrylonitrile/Divinylbenzene Copolymerстатья

Прикрепленные файлы