Structures and properties of Ti alloys after double implantationстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:The paper presents new results on investigation of structure and physical-mechanical properties of near surface layers of titanium alloys after (W(+), Mo(+)) ion implantation and subsequent thermal annealing under 550 degrees C for 2 h. Using back scattering (RBS) of helium ions and protons, scanning electron microscopy (SEM) with microanalysis (EDS), (WDS), proton (ion) induced X-ray emission (PIXE), X-ray phase analysis (XRD) with a grazing incidence geometry (0.5 degrees angle), measurements of nanohardness and elastic modulus, friction wear (cylinder-plate), measurements of corrosion resistance in a salt solution, we investigated the VT-6 samples, and determined their fatigue resistance under cyclic loads. Double increase of hardness, decrease of wear and increased fatigue resistance were found, which was related to the formation of small dispersion (nanodimension) nitride, carbonitride, and intermetalloid phases. (c) 2009 Published by Elsevier Ltd.